Solid State Battery Raw Material
XWELL solid-state battery raw materials are used for advanced battery research and sample development. Material selection depends on cell structure, electrolyte system and process route. Please provide the required material type, specification and experimental application.
LATP Lithium Aluminum Titanium Phosphate Solid Electrolyte Sheet Li1.3Al0.3Ti1.7 PO4
Model:Li₁.₃Al₀.₃Ti₁.₇(PO₄)₃
Dimensions:13×1mm (stock), 6.8×1mm
Density:2.77 g/cm³ (94% theoretical)
Ionic Conductivity:0.7 mS/cm @25°C
Lead Time:In stock (13mm), 1 week (6.8mm)
Applications:All-Solid-State Batteries
Storage:Dry environment (desiccator recommended)
Temperature:25°C
MOQ: 10g
Leading time: 5-7 working days
LLZTO Solid Electrolyte Tantalum Doped Lithium Lanthanum Zirconium Oxygen Li6.5La3Zr1.5Ta0.5O12
Model:LLZTO
Crystal Structure:Cubic garnet (Ia-3d)
Density:95% theoretical (5.1 g/cm³)
Thickness Options:50–300 μm (customizable)
Ionic Conductivity:1.68×10 −3 S/cm (25°C)
Activation Energy:0.25–0.30 eV
Thermal Stability:Up to 1000°C (melting point)
Storage:Argon glovebox (O₂/H₂O <0.1 ppm) to prevent Li₂CO₃ formation
MOQ:10pcs
Leading time: 5-7 working days
LLTO (Lithium Lanthanum Titanium Oxide) Solid Electrolyte Powder
Chemical Composition:Li₇La₃Zr₂O₁₂
Appearance (Powder):White Powder
Average Particle Size:40–60nm
Reference Procedure for Conductivity Testing:200MPa pressure, 1000°C temperature
MOQ: 10g
Leading time: 5-7 working days
Sodium Nickel Manganate MS-PMT-1 — P2-type Sodium-Ion Battery Cathode Material with 117.31mAh/g Capacity, 95% Initial Efficiency, and 1.586g/cm³ Tap Density
Model:MS-PMT-1
Appearance:Black Powder
Specific Surface Area:0.843m²/g
Tap Density:1.586g/cm³
Gram Specific Capacity:117.31mAh/g
Initial Efficiency:95%
MOQ: 200g
Leading time: 5-7 working days
LIC HLIC-1 Li₃InCl₆ (Particle Size: 1-10μm | Ionic Conductivity: 1.5 ms/cm) — Lithium Indium Chloride Halide Solid-State Electrolyte Powder
Model:Li3InCl6
Particle Size:1-10 μm
Theoretical Density:2.56 g/cm³
Appearance (Powder):White powder, uniform, no foreign matter
Ionic Conductivity (Cold Press):＞1.5 mS/cm (25°C, 300MPa)
Electronic Conductivity (Cold Press):＜1×10⁻⁸ S/cm
MOQ: 10g
Leading time: 5-7 working days
LLZTO Li₆.₄La₃Zr₁.₄Ta₀.₆O₁₂ (Ionic Conductivity: 0.1 mS/cm) — Lithium Lanthanum Zirconium Tantalum Oxide Solid-State Electrolyte
Model:LLZTO
Appearance:White powder, uniform, no foreign matter
Ionic Conductivity:＞10⁻⁴ S/cm @25°C
SEM Morphology:Uniform particle distribution
Moisture (ppm):＜500
pH:＜12.50
MOQ: 100g
Leading time: 5-7 working days
LPSCL-Br Sulfide Solid-State Electrolyte – High-Conductivity Lithium Battery Material with ≥99.5% Purity and 1.5-3.0 μm Particle Size
Model:LPSCL-Br
Purity:≥99.5%
Molecular Formula:Li₁.₄PS₄.₁ClBr₀.₆
Particle Size:1.5-3.0 μm
Ionic Conductivity (Cold Press):＞5 mS/cm (25°C, 300MPa)
Electronic Conductivity (Cold Press):＜5.0×10⁻⁸ S/cm³
Tap Density:0.7-1.2g/cm³
Specific Surface Area:1.0-3.5 m²/g
MOQ: 100g
Leading time: 5-7 working days
- 1